TheLa-CosubstitutedSr_（1–x）La_xFe_（12–x）Co_xO_（19）（x=0–0.5）ferriteswithappropriateBi_2O_3additivewerepreparedbyconventionalsinteringmethodandmicrowavesinteringmethodatlowsinteringtemperaturescompatiblewithLTCC（lowtemperatureco-firedceramics）systems,andtheirsinteringbehaviorwaschieflyinvestigated,includingthecrystalstructure,saturationmagnetizationMs,magneticanisotropyfieldHa,intrinsiccoercivityHci,andCurietemperatureTC.ExperimentresultsclearlyshowedthatthepureM-typecrystalphasewassuccessfullyobtainedwhentheLa-Cosubstitutionamountxdidnotexceed0.3.However,thesingleM-typephasestructuretransformedtomultiphasestructurewithfurtherincreasedx,wheretheM-typephasecoexistedwiththenon-magneticphasesuchasα-Fe_2O_3phase,La_2O_3phase,andLaCoO_3phase.AppropriateLa-CosubstitutionimprovedtheMs（〉62emu/g）,Ha（〉1400kA/m）,andHci（〉320kA/m）fortheferriteswithxvaryingfrom0.1to0.3,buttheTCdecreasedwithincreasingsubstitutionamount.Moreover,themicrowavesinteredferritescouldprovidelargerHciandsimilarMscomparedwiththeconventionalsinteredferrites.