摘要
Aplasmaarcwelding(PAW)-tungsteninertgas(TIG)hybridweldingprocessisproposed.AndthispaperinvestigatedthemicrostructureandpropertiesofpurenickelN6jointsbyPAW-TIGhybridwelding.ComparedwiththeconventionalPAWmethod,thecharacteristicofPAW-TIGweldingprocessisthatthereisnointeractionbetweenthetwoarcs.TheadditionofTIGcanenhancetheintrinsichigh-efficiencypeculiarityandthestabilityofthekeyholestatusofPAW.ThejointsmadeusingPAWandPAW-TIG,respectively,weresubjectedtomicrostructuralevaluationsandtensiletestingsoastoanalyzetheeffectofTIGarcenergyonthemicrostructureandmechanicalpropertiesofthesejoints.Theresultsofthisinvestigationindicatethatsignificantgraincoarseningwasobservedintheweldmetal(WM)andheataffectedzone(HAZ)anditisfoundthattheextentofgraincoarseningincreasedwiththeadditionofTIGarc.Andthemicrostructureinhybridjoint,withwiderweldwidthandthesmoothsurface,iscoarserthaninPAWjoint.Furthermore,themicrohardnessandultimatetensilestrength(UTS)ofhybridjointisslightlylowerthanthatofPAWjoint.ThefractographobservationshowsthatthefracturingmechanismofPAWjointsductile,whilethehybridweldingjointsexistsasbrittle-ductilefracturemode.Theoutcomeofthisworkshowsthatintheconditionofsamedepositedrate,TIGarcpost-weldheattreatmentcanimprovetheweldingefficiencyandweldingspeed.TheproposedPAW-TIGhybridweldingprocessisdemonstratedtobesuitableforweldingnickelanditsalloysinindustryapplication.
出版日期
2017年04月14日(中国期刊网平台首次上网日期,不代表论文的发表时间)