摘要
Thecreepmechanismofas-castMg-6Al-6Ndalloywasstudied.Thestressexponentforcreepis5.8undertheappliedstressesof50-70MPaat175°C.Theactivationenergyforcreepis189kJ·mol-1undertheappliedstressof70MPaintherangeof150-200°C.Thetruestressexponentandthresholdstressforcreeparecalculatedas4.96and10.2MPa,respectively.Thetruestressexponentindicatesthatitscreepmechanismbelongstothedislocationclimb-controlledcreep,whichisinagreementwiththemicrostructurechangesbeforeandaftercreep.ThehighvalueforstressexponentisattributedtotheinteractionofAl11Nd3phasewithdislocations.Theactivationenergyismorethantheself-diffusionactivationenergyofMg,whichisattributedtotheloadtransfertakingplacefromthematrixtoAl11Nd3phaseduringcreep.
出版日期
2010年05月15日（中国期刊网平台首次上网日期，不代表论文的发表时间）