简介：ThemechanicalpropertiesofpressurelesssinteringFe-Si3N4bondedSiCandSi3N4bondedSiCwithsamemanufactureprocesshavebeencomparedinthispaper.TheoxidizingmechanismofFe-Si3N4bondedSiCceramicmatrixcompositehasbeeninvestigatedespeciallythroughTG-DSC(thermogravimetricanalysis-differentialscanningcalorimeter)experiment.DuringoxidationprocedurethemainreactionistheoxidationofSiCandSi3N4,SiO2whichformprotectingfilmtopreventfurtheroxidizing.AndresidualironinthesamplesbecomeFe2O3andFe3O4,theoxidationkineticsat1100～1300℃ofre-Si3N4bondedSiChasbeenstudiedespecially.Theweightgainperunitareaatinitialstagechangesaccordingtobeelinerule,inthemiddleaccordingtoconic,andinthelastoxidationperiodfollowsparabolarule.

简介：

简介：Inthepresentpaper,novelsidewallmaterialsforaluminumreductioncellwerepreparedinairusingmagnesiaandmagnetiteasstartingmaterials.ThesinteringbehaviorsofthespecimenswereinvestigatedbymeansofX-raydiffraction(XRD)andscanningelectronmicroscope(SEM).AndcorrosiontestsinaNa_3AlF_6-AlF_3-K_3AlF_6bathwereconductedtoevaluatetheelectrolytecorrosionresistance.TheresultsshowthattheFe_3O_4phaseistransformedintoFe_2O_3athightemperatures,whichinturnreactswiththeMgOaddedtoformMgFe_2O_4spinel.AndwithincreasingtheMgOcontentfrom0to30mass%,densificationofthespecimensdecreasesmainlyduetolargervolumeexpansionresultingfromformationofmoreMgFe_2O_4.ThecorrosiontestsshowthatcorrosionlayersareproducedinalltheMgOaddedspecimens.However,forspecimenscontainingMgFe_2O_4phaseonly,Mg(Al,Fe)_2O_4compositespinellayersarealsogenerated,whichremarkablyimprovethecorrosionresistanceofthespecimens.

简介：