简介:RadiallyorientedNd–Fe–BringmagnetswerepreparedbybackwardextrusionofMQ-Cpowder.Thepunchchamferradiushasagreatimpactonthemicrostructureandmagneticpropertiesoftheringmagnet.Withthechamferradiuschangingfrom2,5to8mm,thecracksintheinnerwalldecreaseobviouslywhilethecrystallographicalignmentdrops.Furthermore,themechanismofcaxisgrowthwassuggestedtobeacombinationofsheardeformationinthecornerandsolution-precipitationunderthestressparalleltoradialdirection.Thealignmentdropsonthetopofringbecausethegrainsgrowfreelyandsometexturedgrainsgrowthroughnucleationandrecrystallization.Inthepresentwork,theoptimalpunchchamferradiusisfoundtobe2mm,andinthiscase,theremanence,coercivity,andmaximumenergyproductoftheringmagnetachieve1.4T,670kJám,and342kJám,respectively.