简介:Ca-dopedBaMgAl10O17:Eu2+,Mn2+(BAM)bluephosphorsweresynthesizedbyfluxassistedsolid-statereactionmethodusingCaF2andBaF2asco-flux.GooddispersityandparticlesizehomogenizationofhexagonalpurephaseBAMwereobtainedbysinteringat1400℃.TheeffectsoftheCa2+ionscontentonthestructure,morphologyandphotoluminescencepropertiesofthephosphorswerestudied.TheresultsindicatedthattheincorporationofCacoulddecreasethelatticeconstant,improvethehomogeneityanddispersityandenhancethephotoluminescence(PL)intensityofthephosphoreffectively.TheoptimumBa0.86Ca0.04Mg0.97Al10O17:0.1Eu2+,0.03Mn2+PLintensitywasenhancedforabout30%andrelativebrightnesswasimprovedabout4%.Furthermore,thesynthesizedBAMandcommercialBAMphosphorswereannealedfor30minat600oCinair.TheCa-dopedphosphorshadstrongeremissionintensity,higherbrightnessandbetterchromaticitystabilitythanthatofthecommercialphosphor.TheseresultsindicatedthatCa-dopedbluephosphorshadgoodpotentialapplicationsinthecommercialtricolorfluorescentlampsaswellasinotherdisplayandlamps.
简介:在823K和973K的条件下,采用恒电流密度共电沉积法在LiCl-KCl-MgCl2-Gd2O3熔盐体系中制备Mg-Li-Gd合金,并运用XRD、SEM、EDS和OM对所制备合金进行微观组织分析。结果表明:在开始的30min内,主要是Mg和Gd的沉积,所得合金含96.53%Mg,3.20%Gd和0.27%Li(质量分数),然后Li迅速沉积。可以通过控制电解时间或改变Gd2O3的浓度调节Mg-Li-Gd合金的组成。XRD分析可知,在Mg-Li-Gd合金中存在Mg3Gd相和Mg2Gd相。从Gd元素的面扫描分析可知,Gd元素主要分布在Mg-Li-Gd合金的晶界处。Gd的添加增强了合金的抗腐蚀能力。
简介:ToevaluatethepossibilityofusingGd-Si-Gealloysinmagneticrefrigerators,samplesofGd-Si-GealloysweremadeofdomesticGd.Themagnetocaloriceffectofsampleswasestimatedbymagneticentropychange(-ΔSm)calculatedfromM-HcurvesaccordingtoMaxwellrelation.ThefirstorderphasetransformationwasdestroyedduetotheimpuritiesinthecommercialGd,sothatnogiantmagnetocaloriceffectwasfound.ThesamplesmadeofpurifiedGdexhibitfirstorderphasetransformation,andthe-ΔSmisbasicallyconsistentwiththepublisheddataofAmeslaboratory,USA.ThisworkprovesthatGd-Si-GealloysmadeofdomesticGdcanbeutilizedinmagneticrefrigerators.
简介:摘要随着社会经济不断发展,我国印染行业发展迅速,无论是印染规模还是印染技术,均得到了长足的发展和提高,印染废水产生量日益增多,印染废水污染物组成也愈发复杂,相应提高了对于印染废水回用技术的实际要求。但就我国印染行业当前的印染废水回用现状来看,其废水回用技术仍以传统二级生物处理工艺为主,面对污染物更加复杂、结构更加稳定的现代印染废水,表现出较明显的不适应性和局限性。在这种环境背景下,笔者就A2/O-O3-BAF工艺在印染废水回用中的应用进行了试验探索,试验结果表明,A2/O-O3-BAF工艺可有有效处理印染废水中的复杂污染物,使其达到废水回用相关标准要求,具有较好的经济性和适用性。
简介:Sr1.995–1.5xGdxSiO4:0.005Eu2+phosphorserieswithx=0–0.08molfornear-ultravioletwhitelight-emittingdiodes(NUVw-LEDs)weresynthesizedviasolid-statereactionmethod.XRDprofilepatternandrefinementresultsdemonstratedthatdopingGd3+ionsresultedinthephasetransformation(β-Sr2SiO4→α’-Sr2SiO4).Thephotoluminescencespectrumofthesamplewithx=0moldisplayedtwoemissionpeakscenteredat470and525nm.Thetwo-peakspectrabecameone-peakspectrawiththeGd3+concentrationincreasing.Actually,thefittingresultsdemonstratedthattheone-peakspectrawerestillcomposedoftwosingleemissionspectra.ThephotoluminescenceintensitywasimprovedandtheCIEchromaticitycoordinateswereadjustedviadopingGd3+.
简介:WehavesynthesizedandinvestigatedphysicalpropertiesoftwonewquaternarycompoundsGd2CoAl4T2(T=Si,Ge)singlecrystals,whichareisostructuraltoTb2NiAl4Ge2andEr2CoAl4Ge2.Themostimportantstructuralfeatureofthesematerialsistheanti-CaF2-typeCoAl4T2slabs.Thesematerialsshowmetallicbehaviorbelow300Kandthereisalong-rangeantiferromagnetic(AFM)transitionappearingat20and27KforGdCoAl4Ge2andGd2CoAl4Si2,respectively.ResistivityandheatcapacitymeasurementsalsoconfirmthesebulkAFMtransitions.Furtheranalysisindicatesthatthislong-rangeantiferromagnetismshouldresultfromthemagneticinteractionbetweenlocalmomentsofGd^3+ions.
简介:Aseriesofoxygenpermeabledual-phasecompositeoxides60wt%Ce0.8Gd0.2O2-δ-40wt%LnBaCo2O5+δ(CGO-LBCO,Ln=La,Pr,Nd,Sm,GdandY)weresynthesizedthroughasol-gelrouteandeffectsoftheLn3+cationsontheirphasestructure,oxygenpermeabilityandchemicalstabilityagainstCO2wereinvestigatedsystemicallybyXRD,SEM,TG-DSCandoxygenpermeationexperiments.XRDpatternsrevealthatthelargerLn3+cations(La3+,Pr3+andNd3+)successfullystabilizedthedouble-layeredperovskitestructureofsinteredLBCO,whilethesmallerones(Sm3+,Gd3+,andY3+)resultedinthepartialdecompositionofLBCOwithsomeimpuritiesformed.CGO-PBCOyieldsthehighestoxygenpermeationflux,reaching2.8×10-7mols-1cm-2at925?Cwith1mmthicknessunderair/Hegradient.TheTG-DSCprofilesin20mol%CO2/N2andoxygenpermeabilityexperimentswithCO2assweepgasshowthatCGO-YBCOdemonstratesthebestchemicalstabilityagainstCO2,possiblyduetoitsminimumbasicity.ThestableoxygenpermeationfluxofCGO-YBCOunderCO2atmosphererevealsitspotentialapplicationintheoxy-fuelcombustionrouteforCO2capture.
简介:阶段和磁电机在合金R(Co_(1-x)Sn_x)的热量的效果有x=的_20,0.025,0.050,0.075,和0.100被X光检查衍射分析和磁化测量调查。在RCo_2的Sn的替换是有限的。为RCo_2的合金的立方的MgCu_2-typestructure被X光检查粉末衍射证实,留下的合金主要由RCo_2阶段组成了,与一些RCo_3和R_5Sn_3杂质阶段一起。Theimpurity阶段随Sn内容的增加增加。合金的T_c不对为Dy(Co_(1-x)Sn_x)的Sn替换很敏感_2和Tb(Co_(1-x)Sn_x)_2inGd(Co_(1-x)Sn_x)_2,居里温度显著地增加。最大的磁性的熵在合金Dy(Co_(1-x)Sn_x)改变_2(x=0,0.025,0.050,0.075)是5.78,5.43,3.88,并且2.98J·kg~(-1)·K~(-1),分别地,并且那些在Tb(Co_(1-x)Sn_x)_2(x=0,0.025)是3.44,and2.29J·kg~(-1)·K~(-1)分别地0-2.0T在应用的地里变化。
简介:摘要针对曝气生物滤池在设计和建设过程出现的反冲洗、曝气、滤料选取等多重问题,分别进行阐述,结合作者的实践经验,探讨了曝气生物滤池设计和施工中的注意事项,供设计该工艺时参考。以使曝气生物滤池工艺的成熟设计尽快得到推广和应用,避免盲目套用设计手册或由于实际经验缺乏造成工艺隐患。