简介:Al-5Ti-0.5C-8Sr(集体部分,%)主人合金用一个melt反应方法被准备。微观结构和主人合金的合成过程被光显微镜学,X光检查衍射,扫描电子显微镜学和X光检查调查精力散的光谱。结果证明主人合金由组成一(艾尔),TiAl3,TiC,Al4Sr和Al-Ti-Sr分阶段执行。主人合金的合成机制如下:TiAl3通过在K2TiF6和艾尔之间的反应被形成在基础材料的部分融化层融化在850个C粒子与同类地分布式的加强在超声的行动和一张契约下面被变成液体filler在团结以后被获得。体积部分原文如此,在契约的粒子能被改变以铜锌金焊接的温度改变。最大值原文如此,契约材料的粒子体积部分在brazi到达了37%?
简介:ThesubmicronpowdermixturesofTiC-TiN-WC-Mo-C-Nisinteredat1400℃orbelowinvacuumwerestudiedbyX-raydiffraction(XRD),scanningelectronmicroscopy(SEM)andtransmissionelectronmicroscopy(TEM)analyses.TheresultsshowedthatMo2Cformedat800℃orbelow.BothWCandMo2Cdisappearedat1200℃,andTiNdisappearedat1250℃.Inaddition,thevariationsoflatticeconstantsofthetitaniumcarbonitrideandnickelbinderphasewithsinteringtemperaturewereexperimentallyobtained,andthereasonwasanalyzed.
简介:2007年3月26日奥兰多讯:在2007’美国CTIA无线通信展上,德州仪器首度公开展示了一款指尖般大小的DLP微型投影机样机。DLP微型投影机既可独立单机投影,也可置入移动设备,实现了用大屏幕观看手机、数码照相机和手提媒体播放器视频内容的梦想。
简介:以二不同纯净的Zr开始,基于Ti的体积有Ti40Zr25Cu12Ni320被准备。在形成合金的能力(GFA)的玻璃上的0.2at.%,0.4at.%,0.5at.%,0.6at.%,和1at.%的层次的钇的增加的效果借助于金属组织学,X光检查衍射,和微分扫描热量测定被调查了。试验性的数据显示高杂质内容戏剧性地减少形成能力的玻璃。有0.5at.%Y的Microalloying在压制水晶的阶段形成并且在低纯净的合金减轻氧的有害效果是有效的。相反在包含高纯净的元素的合金,有效的钇增加是不到0.4at.%。结果显示最佳掺杂物的有益的效果主要由于清除是经由无害的阶段的形成的氧杂质。
简介:Howtocontrolmeltcompositionisthekeyforgettinghighqualityalloymelt.Thepapermadethefollowingefforts:(1)TheactivitycoefficientsinTi-15-3melthavebeencalculated.(2)Takingadvantageoftheactivitycoefficients,theevaporationlossesofcomponentsinTi-15-3meltduringISMprocesshavebeenstudied.Thecalculatedresultsshowthatthereisacriticalvacuumdegree(about1.33Pa)duringmeltingprocess.
简介:Thisstudyexaminesmechanismsforprovidingnucleitoequiaxedgrainsintheweldsofpureferriticstainlesssteel(FSS).TheadditionofthealloyelementTitopureFSS439causestheprecipitationofTiN,whichcanbenefitthecolumnar-to-equiaxedtransition(CET)ofgastungstenarcwelding(GTAW).Meanwhile,theinitialmorphologyoftheprecipitates,theconcentrationmultiplicationsofTi,N,etc.ofFSS439shouldbecontrolledtoinducetheformationofCETduringtheshortweldingprocess.
简介:Ti-dopedW03filmswerepreparedbythemid-frequencydual-targetmagnetronsputteringmethod.ThestructureandelectrochromicpropertiesoftheTi-dopedWO3filmswereanalysedbyX-Raydiffraction(XRD),Ramanspectroscopy,spectrophotometer,cyclicchronoam-perometryandatomicforcemicroscopy(AFM).Theresultsindicatethatthecrystallinitydecreaseafterthedopingoftitanium,thechannelsforioninjectionandextractionincrease,therespondingspeedwith5.1%titaniumdopedbecomesfaster,anditscirclelifeincreasesmorethanfourtimescomparedwiththeundopedWOafilm.Inthecolouredstate,theW-O-Wbondsdecrease,buttheW=Obondsincrease.SincetheW-O-WbondsbreakdownforLi~+ions'injectionandmoreW=Obondsform,itismoreconvenienttoinjectLi~+ionsintotheTi-dopedfilmthanundopedfilmbecausemoreW-O-Wbondsbreakdowninthecolouredstate.