简介:Asanodematerialsforlithium-ionbatteries,SiO_2isofgreatinterestbecauseofitshighcapacity,lowcostandenvironmentalaffinity.AfacileapproachhasbeendevelopedtofabricateSiO_2@Chollowspheresbyhydrolysisoftetraethylorthosilicate(TEOS)toformSiO_2shellsonorganicspheretemplatesfollowedbycalcinationsinairtoremovethetemplates,andthentheSiO_2shellsarecoveredbycarbonlayers.ElectronmicroscopyinvestigationsconfirmhollowstructureoftheSiO_2@C.TheSiO_2@ChollowsphereswithdifferentSiO_2contentsdisplaygradualincreaseinspecificcapacitywithdischarge/chargecycling,amongwhichtheSiO_2@CwithSiO_2contentof67wt%exhibitsdischarge/chargecapacitiesof653.4/649.6mAhg~(-1)over160cyclesatcurrentdensityof0.11mAcm~(-2).TheimpedancefittingoftheelectrochemicalimpedancespectroscopyshowsthattheSiO_2@CwithSiO_2contentof67wt%hasthelowestchargetransferresistance,whichindicatesthattheSiO_2@Chollowspheresispromisinganodecandidateforlithium-ionbatteries.
简介:Epoxyresin/Ni@Cnanoparticlecompositeswithalignedmicrostructurewerepreparedbyusingaprocedureofmagneticfieldassistedcuring.Theresultsshowthattheresistivityofcompositesexhibitsnegativetemperaturecoeffcient(NTC)effectaboveroomtemperature,andcanbeadjustedbyvaryingthecontentfillerandthemagnitudeofmagneticfieldapplied.Hill'squantumtunnelingmodelwasmodifiedtounderstandtheelectricalconductionmechanisminthecomposites.ItshowsthattheNTCeffectascribestothedominantthermalactivatedtunnelingtransportofelectronacrossadjacentnanoparticles,aswellasthelowthermalexpansivityofepoxyresinmatrix.
简介:有alloying原子X=C,B,N,O和空缺的镁和它的合金的概括叠的差错(GSF)精力和表面精力用第一原则的方法被调查了。叠的差错精力上的alloying原子和空缺的占优势的减少效果在slip飞机附近在第一层从他们的位置被结果,这被发现。叠的差错精力是将近与纯镁一样当alloying原子和空缺被放在时第二,第三,第4,第5和第6层。O强烈减少Mg的GSF精力,这被显示出。alloying原子C,B和N增加表面精力,但是O和空缺减少Mg的表面精力。Mg和Mg合金的韧性被使用在表面精力和不稳定的叠差错精力之间的比率基于瑞斯标准讨论了。
简介:YogabookC930是世界上最薄的双屏幕笔记本电脑,拥有LCD屏幕和E-ink屏幕,轻薄设计更充分表现了其科技性,双屏幕显示的方式更体现了方便的使用性,独特的转轴使得产品的使用性和方便性得到最佳的“使用体验”。其标配的蓝牙触控笔具有4096级压感并支持倾斜功能。YogabookC930是一款多模式设备,可转化成平板电脑模式和E-ink电子书模式。E-ink可在键盘和书写功能之间转换,书写内容能以多种格式应用到LCD屏幕上各类软件里,书写文字可一键转化成键盘所打字体。产品采用极简设计,unibody的设计方式,将所有复杂结构隐藏在极简外表之下,从外观完全看不到分件和螺丝。
简介:钡锶铝矽酸盐(BSAS)和Si/BSAS涂层经由一个二拍子的圆舞激光cladding过程在C/SiCcomposites的表面上被制作。微观结构,机械性质,和样品的水蒸汽腐蚀行为被调查。BSAS涂层被发现紧被结合到底层和仅仅一些毛孔,microcracks被观察。硅中间层的介绍被揭示减少热应力并且支持在激光cladding过程期间形成的缺点愈合。为了评估腐蚀抵抗,BSAS和Si/BSAS-coated,C/SiCcomposites暴露于50%H2在1250敢椠?慦桳潩的O和50%O2吗?
简介:采用热注入法成功制备出三元AgInS2和四元Ag—Zn—In—S量子点,物性测试得到AgInS2量子点的发射峰为701nm,Ag—Zn—In—S量子点的发射峰593nm,即Ag-Zn-In—S量子点的发射峰相对于AgInS2量子点发生了蓝移,AgInS2和Ag—Zn—In—S量子点都表现出了较长的荧光寿命,分别为169ns和162ns,结合生物组织光学窗口范围限制,相对Ag—Z—In—S,AgInS2量子点更适用于生物标记。
简介:Basedontheclassicdiffusioncontrollednucleationandgrowththeory,thesympatheticnucleationledgewisegrowthmechanismofbainitewasstudiedtheoreticallyforIowcarbonFe-Calloys.Therationalityoftheoccurrenceofsympatheticnucleationontheterracesofledgescompetingwithlateralledgegrowthandothersitesnucleationwasdemonstratedbythepresentworkquantitatively.ThecalculationsindicatedthatIowreactiontemperaturesandhighcarbonconcentrationsmayfavorthesympatheticnucleation,thusaccountingfortheformationofmultilayerstructuresofbainite.
简介:石墨和ZrB2–SiC的氧化行为修改了石墨合成在1×105Pa空气和0.2×105PaO2。氧化测试在一个感应的加热炉子被进行。这二材料的氧化跟随了线性率法律。在2100°C的石墨和C–ZrB2–SiC的坚定的半径损失率在1×105−2和1.05×10−2%/s>Pa空气,和3.23×10−2和2.21×10在0.2×105−2%/s>PaO2,分别地。ZrB2并且原文如此的加入显著地减少了石墨的氧化率因为在氧化期间在样品表面上形成的氧化物规模在减少暴露的表面区域帮助在下面底层。在有一样的氧的二不同气氛部分压力,石墨和C–ZrB2–SiC在0.2×105PaO2比在1×105Pa空气。氧化为石墨和C–ZrB2–SiC的控制率的步被建议分别地是通过边界层并且通过在氧化物规模的毛孔的氧的里面的散开。一个模型基于散开理论被建立在他们的氧化行为上讨论全部的煤气的压力的效果。
简介:弧与cored电线喷洒被使用在低碳钢底层上扔FeMnCr/Cr3C2涂层,也就是FM1,FM2和FM3。涂层的热吃惊电阻被调查在热吃惊抵抗上估计Cr3C2内容的影响。在热骑车测试下面的涂层的特征被光显微镜学,地排放扫描电子显微镜(FE-SEM)和精力分散光谱(版本)学习,X光检查衍射(XRD)。试验性的结果证明涂层的坚硬增加,结合力量随涂层的Cr3C2内容的增加稍微减少。作为结果,FM2涂层拥有最好的热吃惊抵抗,归因于它比那些的更好热的扩大火柴和FM3涂层的wettability,更少的氧化物率比FM1涂层在涂层从裂缝形成和繁殖制止的。
简介:德国Ⅵ系统公司宣布研制出第一个通过多模光纤数据传输速率达40吉比特/s(40Gbit/s)的单VCSEL(垂直腔面发射激光器)。2009年1月份在美国加州SanJose召开的光子学会议上,该公司刚介绍了其20吉比特/s的器件,目前又使它的量子点激光器的调制速率提高了1倍。该公司利用其VCSEL和PIN光探测组件实现了通过多模光纤的40吉比特/s连续传输,这是850hm(波长)光发射的刨记录器件,是用与20吉比特/sVCSEL相同的光刻掩模研制的,但对外延结构作了改进。这种器件设计利用GaAs量子阱中的InAs量子点,并嵌入到AlGaAs基体中。
简介:Overcasting是过去常生产铝(固体)的一种新有点不一样的加入技术结合的/magnesium(液体)在这研究的二金属的材料。为Al/Mg(A390/AM60)二金属的样品,接口微观结构是研究点,它直接影响机械性质。因此,发现一个方法改进接口微观结构具有重要重要性。这研究在二金属的样品的A390/AM60接口微观结构上在液体Mg合金和热处理在钙(Ca)的效果上集中了增加。严峻的结果证明与在AM60的Ca增加,由于二个可能的原因,接口微观结构和A390/AM60二金属的样品的shear力量能被改进。热处理能进一步由溶解-Mg17Al12进-Mg并且破坏Mg2Si层结构。
简介:Inthisstudy,Almatrixcompositesreinforcedby7.5and15vol.%B4CparticlesandalsomonolithicAl(AlwithouttheB4Cparticles)wereproducedbywetattritionmillingandsubsequenthotforwardextrusionprocesses.Themicrostructureofthecomposites,evaluatedbyscanningelectronmicroscopy(SEM),showedthattheB4CparticleswereproperlydistributedintheAlmatrix.MechanicalpropertiesoftheAI/B4CcompositesandmonolithicAlwereinvestigatedbytensile,wearandhardnesstests.TheresultsrevealedthatwithincreasingcontentofB4Cparticles,thetensilestrengthandmicrohardnessofcompositesincreasedbuttheelongationdecreased.Inaddition,thetensilestrengthandmicrohardnessofcompositesampleswerehigherthanthoseofmonolithicAl.ThedensitymeasurementsrevealedthatthedensityofcompositesdecreasedwithincreasingcontentoftheB4Cparticles.