简介：Precipitationstrengtheningaswellassolutionstrengtheningiskeymechanismforheatresistantsteels.Itisveryimportanttocharacterizetheprecipitatesin9%Crferriteheatresistantsteels,especiallytoshowthenanometer-sizedparticles.Bytransmissionelectronicmicroscopeattachedwithanenergydispersivespectrometeraswellasopticalmicroscope,scanningelectronicmicroscope,themicrostructureandchemicalcompositionofprecipitatesina9%Crheatresistantsteelafterdifferentheattreatmentswereinvestigated.ItwasfoundthatthemicrostructureofnormalizedsamplewasmartensitewithfineNbCandFe3C.Themicrostructureoftemperedsampleistemperedmartensite,andtheremainlyweretwotypesofprecipitates,M23C6withthesizerangeof50-300nmandMXwiththesizeof10-100nm.SuperfineM23C6precipitatedpreferablyonpriorausteniticgrainboundariesandmartensiticlathboundaries,whilenanometer-sizedMXprecipitatesweredistributedrandomly.Aftershort-termcreep,Lavesphaseformedalonggrainboundariesofthe9%Crsteel,andM23C6andMXprecipitateswerefoundtobecomecoarser.Moreinformationaboutprecipitatesinthe9%Crsteelhadbeenexhibitedbyatomicforcemicroscopy.Thereby,distribution,sizeandshapeoftheprecipitatesaswellastheircompositionsandstructureswererevealed.
客服QQ：30444492琼网文【2021】1550-113号
增值电信业务经营许可证：琼B2-20210322
出版物经营许可证：新出发龙华出字第(2021)009号
广播电视节目制作经营许可证：(琼)字第00779号
版权所有 ©2002-2024 期刊网(www.qikanchina.com) 琼ICP备2021005105号