Continuoussiliconcarbidefiberreinforcedsiliconcarbide(SiCf/SiC)compositeshavebeenconsideredtobecandidatematerialsofhightemperaturestructuralapplicationinaerospace,energyconservationandpowergenerationduetotheexcellenthightemperaturemechanicalproperties,goodfractureresistance,corrosionresistanceandthermodynamicstability.Furthermore,duetothehighthermalstability,lowinducedradioactivity,quickdecayofactivityandlowafterheat,SiCf/SiCcompositeshavebeenrecognizedasthepromisingmaterialsoffissionandfuturefusionreactors.SiCf/SiCcompositesarecomposedofSiCfiberandSiCmarixmaterials.Radiationresistance,oxidationtolerance,fracturetoughnessandtensilestrengthofSiCfiberhaveadirectimpactontheSiCf/SiCcompositesperformance.