简介:摘要为了实现窗户的自动启闭,方便人们的日常生活,采用DS18B20温度传感器为温度采集元件,单片机STC12C5A32S2为主控制模块,将温度采集元件获得的温度参数经STC12C5A32S2处理后,通过步进电机驱动器控制步进电机来实现窗户的自动启闭。给出了系统的原理方框图、软件设计流程图,搭建了电路,样机测试结果表明,基于STC12C5A32S2的自动开窗控制系统操作简便、系统运行稳定,提高了家居环境空气质量,可推广到宾馆、医院及智能农业、工业生产领域。
简介:Inpursuingexcellentsupercapacitorelectrodes,wedesignedaseriesofM0S2/C0S2compositesconsistingofflower-likedMoS2andoctahedron-shapedCoS2throughafacileone-stephydrothermalmethodandinvestigatedtheelectrochemicalperformanceofthesampleswithvarioushydrothermaltime.Duetothecouplingoftwometalspeciesandabigamountofwell-developedCoS2andMoS2,theresultsindicatedthattheMoS2/CoS2compositeselectrodesexhibitedthebestelectrochemicalperfor-mancewithalargespecificcapacitanceof490F/gat2mV/sor400F/gat10A/gamongallsamplesasthehydrothermaltimereached48h(MCS48).Furthermore,theretentionofMCS48is93.1%after10000cyclesat10A/g,whichmanifeststheexcellentcyclingstability.TheoutstandingelectrochemicalperformanceofMCS48indicatesthatitcouldbeaverypromisingandnovelenergystoragematerialforsupercapacitorsinthefuture.
简介:为进一步提高涂层C/C复合材料的高温抗氧化性能,设计C/C复合材料SiC-MoSi2-TiSi2复合涂层,在实验室分二次进行包埋,制作该复合材料表面完整的多组分复合多层涂层,测试该涂层在1773K高温下的抗氧化性能并对其高温抗氧化机理进行分析。结果表明,在选择的实验条件下,二次包埋法制备的C/C复合材料SiC-MoSi2-TiSi2复合涂层在1773K有氧环境下具有良好的抗氧化性能,失效时间可以延长至79h。该涂层抗氧化性能的提高是因为涂层SiC结构中的孔洞和裂纹有效地被MoSi2和TiSi2所填充,而且高温氧化时在涂层表面形成致密、连续、稳定的玻璃质氧化物。
简介:摘要TN-C-S接地方式是低压配电系统一种接地系统,因系统简洁节省材料而且运行稳定,被广泛的应用在住宅小区、群体建筑、施工现场临时用电等的低压配电系统。但是,如果TN-C-S接地系统施工时,未按规范要求去施工,接线错误,那么当某个局部发生电气事故时,将会影响到整个低压配电系统用电安全,严重时会造成烧毁成片用电设备。本文将对TN-C-S接地系统的保护原理、目前施工中存在的安全隐患以及会导致的安全后果进行分析研究,并给出的正确的施工方法。