简介：ProblemsaboutsurfacemountingprocessforfinepitchdevicesandreasonsonsolderbridgingofLtypeleaddevicesweldedaredepicted.Bridgingmechanismandinfluencefactorsareanalyzedwithtwo-dimensionalgeometricmodel.Basedonthis,high-densitysurfacemounttechnology(SMT)forfinepitchLtypeleaddevicesheatedbyscan-ninglaserisraised.SurfacemountprocessforQFP208onprintedcircuitboard(PCB)isstudied.Theresultsoftestsarethatitisquitepossibletosolvethesolderbridgingofsurfacemountingforpitchdeviceswithscanninglaser-heat-ingmethod.

简介：904L是一种全奥氏体不锈钢,在焊接时易出现热裂纹,且晶间腐蚀和应力腐蚀开裂倾向较大。本文经可焊性分析后,从焊接材料和焊接工艺参数的选择入手,进行了焊接工艺性试验,找出了合适的焊接规范,并在实际产品的焊接中进行了严格的质量控制,生产出合格的产品。

简介：

简介：Intheacceleratordrivensub-criticalsystem(ADS)cooledbyliquidPbBialloy,theausteniticstainlesssteel316Lisoneofthecandidatesofstructuralmaterials.However,thecorrosionandwearbehaviorof316Lsteelinthehigh-velocitystreamofliquidPbBiisthemostessentialissue,whichisurgenttobepaidcloseattention.Inordertoacquirethemorphologyandmechanicalpropertiesof316Lsteelintheconditionsofdifferentrelativeflowingvelocity(RFV),respectively2.62m/s,3.69m/s,4.77m/s,theexperimentwascarriedoutindynamicliquidPbBiat550℃,uptoabout1500h.Accordingtotheresults,thesurfaceof316LhasbeencorrodedbadlyandtheelementsofNi,Cr,etc.werefoundtodissolvealot.WiththeincreaseoftheRFV,thefeatureof316Lsurfacechangedfromthesurfacewithmuchdeeperpitsandlooserstructurestotherelativeplanarone,andthethicknessoftheouteroxidelayerdecreasedgraduallywhilethatoftheinneroxidelayerdiminishedalittle,andthemicrohardnessoftheoutermostsubstratealsodeclinedincreasingly,inaddition,thedomainofthepartialsubstratewithitsmicrohardnessbeingaltereddeepenedfurther.Theseexperimentaldatawouldoffertheoreticalbasisandpracticalvaluestostudycorrosionconditionof316LsteelinliquidPbBiwithhigh-velocity.